Polymer blend composition for automotive flooring applications

ABSTRACT

A polymer blend composition, in an exemplary embodiment, includes an impact modified polypropylene copolymer, and a low density polyethylene polymer. The ratio of an amount, by weight, of the impact modified polypropylene copolymer to an amount, by weight, of the low density polyethylene polymer is between about 6:4 to about 9:1.

BACKGROUND OF THE INVENTION

The field of the invention relates generally to a polymer blend composition, and more particularly to a polymer blend composition containing an impact modified polypropylene and a low density polyethylene that can be used to manufacture a non-carpeted automotive flooring material.

Automobile manufactures require that non-carpeted flooring material have scratch and mar resistance, low gloss, and grain definition, while being colorable, durable, and able to withstand large temperature changes without failure. In addition, automobile manufactures require that the flooring material has a low modulus (elasticity) for ease of installation into a vehicle.

Known non-carpeted flooring material are manufactured from blends of impact modified polypropylene and high melt strength polypropylene (partially crosslinked). The impact modified polypropylene creates flexibility to facilitate installation into a vehicle and contributes to low gloss, while the high melt strength polypropylene facilitates scratch and mar resistance, and provides adequate strength during a thermoforming process. However, these known flooring materials have a narrow window of temperature range for thermoforming. High crystallinity of the material leads to sharp drop-off in melt strength during the thermoforming process. In addition, these known flooring materials also significantly increase in gloss as forming temperatures are increased which does not meet automobile manufactures requirements.

BRIEF DESCRIPTION OF THE INVENTION

In one aspect, a polymer blend composition is provided. The polymer blend includes an impact modified polypropylene copolymer, and a low density polyethylene polymer. The ratio of an amount, by weight, of the impact modified polypropylene copolymer to an amount, by weight, of the low density polyethylene polymer is between about 6:4 to about 9:1.

In another aspect, a sheet of automotive flooring material is provided. The sheet of automotive flooring material is made from a polymeric material. The polymeric material is formed from a polymer blend composition. The polymer blend includes an impact modified polypropylene copolymer, and a low density polyethylene polymer. A ratio of an amount, by weight, of the impact modified polypropylene copolymer to an amount, by weight, of the low density polyethylene polymer is between about 6:4 to about 9:1.

In another aspect, a method of making an automotive flooring article is provided. The method includes providing a polymer blend composition, heating the polymer blend to a temperature of about 340° F. to about 380° F., extruding the heated polymer blend to form a sheet of automotive flooring material, and cooling the sheet of automotive flooring material. The polymer blend includes an impact modified polypropylene copolymer, and a low density polyethylene polymer. A ratio of an amount, by weight, of the impact modified polypropylene copolymer to an amount, by weight, of the low density polyethylene polymer is between about 6:4 to about 9:1.

DETAILED DESCRIPTION OF THE INVENTION

A polymer blend composition, an automotive flooring article, and a method of making the automotive flooring article is described below in detail. The polymer blend composition includes an impact modified polypropylene and a low density polyethylene that can be compounded into pellets or converted into sheet material. Sheets made with this blend are thermoformable, colorable, have low modulus elasticity, and low-gloss. The sheets can be grain embossed during the sheet manufacture or the grain can be added during a thermoforming process. The polymer blend composition is used in making non-carpeted automotive flooring articles, for example automotive flooring sheets. In addition, the polymer blend permits recycled blend material to be added back into the blend. Recycled concentrations up to about 50% can be used in the polymer blend and still maintain all the aesthetics and physical properties of the flooring article made from a polymer blend without recycled material. Surprisingly, automotive flooring articles made from the polymer blend maintains low gloss after thermoforming, have excellent hot strength in thermoforming, has low-temp flexibility (down to about −30° F.) and can utilize up to about 50% recycled blend material without adversely affecting the aesthetics or physical properties of the flooring articles.

In an exemplary embodiment, an automotive flooring article is formed from a polymer blend composition that includes an impact modified polypropylene and a highly branched low density polyethylene. A ratio of an amount, by weight, of the impact modified polypropylene copolymer to an amount, by weight, of the low density polyethylene polymer is between about 6:4 to about 9:1, and in another embodiment, between about 7:3 to about 8:2. The polymer blend composition may also include up to about 15 percent by weight of a mineral filler, the percent by weight based on the total weight of the composition. Suitable mineral fillers include, for example, limestone and barites. In one embodiment, the mineral filler is ground to a 325 Mesh. In other embodiments, higher or lower Mesh grinds can be used.

It should be understood that as used herein, “formed from” denotes open, e.g., “comprising”, claim language. As such, it is intended that a composition “formed from” a list of components be a composition that includes at least these recited components, and can further include other, non-recited components, during the composition's formation, for example, UV absorbers; surfactants; processing aids, for example, calcium stearate; pigments, for example, carbon black; antioxidant stabilizers, for example, Irganox B225, commercially available from Ciba Geigy; and the like.

The impact modified polypropylene copolymer is a polypropylene modified with an EPDM rubber, a styrene butadiene rubber or an isoprene rubber. In particular, the impact modified polypropylene copolymer is formed from a propylene monomer and a ethylene propylene diene monomer (EPDM), a styrene butadiene monomer, or an isoprene monomer.

The impact modified polypropylene copolymer has a melt flow index measured at 230° C. of about 0.1 g/10 min to about 10 g/10 min. The low density polyethylene polymer has a melt flow index measured at 190° C. of about 0.1 g/10 min to about 10 g/10 min.

The automotive flooring article, for example, a non-carpet floor liner, a trunk liner, and floor mats, are formed by mixing the ingredients of the polymer blend composition. Specifically, in an exemplary embodiment, an impact modified polypropylene copolymer, a low density polyethylene, a mineral filler, an antioxidant stabilizer, a processing aid, for example calcium stearate, and carbon black are mixed together at a temperature of about 340° F. to about 380° F. The blended polymer composition is then extruded through an extruder having a steam jacket temperature of about 310° F., and the composition is extruded through a die at a temperature of about 380° F. to about 410° F. to form a sheet of flooring material. The extruded sheet material is passed through opposing calender rolls to adjust the thickness of the extruded sheet material to between about 1 mm to about 5 mm. Optionally the extruded sheet material can be embossed at about 800 psi to about 1000 psi at a sheet temperature of about 300° 1 to about 340° F. In another embodiment, the flooring sheet can be embossed during a thermoforming process. After the flooring sheet has been calendered and optionally embossed, the flooring material is cooled with air and/or water, and trimmed to size. The flooring material can be cut into individual sheets or rolled into a continuous roll of flooring material. The flooring material trimmed off the sheet can be recycled by regrinding the material, and adding the reground material to the polymer blend composition up to about 50 percent by weight of the polymer blend composition.

To form a finished flooring article, the flooring material is heated to about 320° F. to about 360° F. and then the hot sheet is placed in a mold mechanically or by hand. The hot sheet is then thermoformed by any suitable thermoforming process, for example, vacuum forming, thermo-stamping, and compression molding. In one embodiment, the mold surfaces have an embossing pattern etched into the surface to emboss the flooring material during the thermoforming process. The thermoformed flooring article is cooled and cut to size. The material trimmed from the flooring article can be reground and recycled by adding the reground flooring material to the polymer blend composition. The polymer blend composition can include up to about 50% of recycled material without any degradation to the properties of the resultant flooring article as compared to a flooring article made from a virgin polymer blend composition. In addition, the flooring material has a gloss of about 8 or less both before and after thermoforming. If the flooring material is embossed, the gloss is about 3 or less before and after thermoforming. Gloss is measured at a 60° angle using any known gloss meter, for example, a Nova-Gloss meter manufactured by Gretag-MacBeth Corporation.

The polymer blend composition will be further described by reference to the following examples which are presented for the purpose of illustration only. Unless otherwise indicated, all amounts are listed as parts by weight.

EXAMPLES

Two different formulations of the polymer blend compositions described above were compared to a control formulation containing an impact modified polypropylene copolymer. Table I below shows the formulations of Examples I, II, and III. Examples I and II are examples of the polymer blend compositions described above. Example III is a comparison example of a formulation that includes an impact modified polypropylene.

TABLE I Formulation I II III Impact Modified Polypropylene¹ 75 72 100 LDPE² 25 23 0 Limestone (325 Mesh) 0 5 0 Carbon Black 2 2 2 Antioxidant³ 0.5 0.5 0.5 Calcium Stearate 0.2 0.2 0.2 ¹Hifax CA10A, an impact modified polypropylene commercially available from LyondellBasell, Inc. ²ATEVA 505 LDPE, commercially available from AT Plastics, Inc., Edmonton, Alberta, Canada. ³Irganox B255, commercially available from Ciba Geigy Corporation.

Each of the formulations of Examples I, II, and III were extruded through an extruder having a steam jacket temperature of about 310° F., and then extruded through a die at a temperature of about 360° F. to form a sheet of flooring material. Half of the sheets of flooring material formed from each of the formulations of Examples I, II, and III were embossed, and the other half of the sheets were left unembossed. The gloss of each sheet was measured at 60° with a Nova-Gloss meter manufactured by Gretag-MacBeth Corporation. The sheets of flooring material were then thermoformed by heating the sheets to about 330° F. and then each hot sheet was placed in a mold, vacuum formed, and then cooled. The gloss of each sheet was again measured at 60°. Table II below shows the average gloss readings for each formulation of Examples I, II, and III.

TABLE II GLOSS at 60° I II III Extruded Sheet Embossed 1.5 1.2 1.3 Unembossed 2.2 1.9 9.5 Thermoformed Sheet Embossed 1.7 1.5 10.1 Unembossed 2.4 2.1 29.0

Examples I and II exhibited a 60°gloss of less than 8 on unembossed sheets, and a 60° gloss of less than 3 on embossed sheets before and after thermoforming. Comparison Example III exhibited a large increase in gloss after thermoforming. Specifically, the 60° gloss of embossed sheets increased from 1.3 before thermoforming to 10.1 after thermoforming. In addition, the 60° gloss of unembossed sheets increased from 9.5 before thermoforming to 29.0 after thermoforming.

The automotive flooring articles made from the polymer blend compositions described above maintain low gloss after thermoforming, have excellent hot strength in thermoforming, has low-temp flexibility (down to about −30° F.) and can utilize up to about 50% recycled blend material without adversely affecting the aesthetics or physical properties of the automotive flooring articles.

This written description uses examples to disclose the invention, including the best mode, and also to enable any person skilled in the art to practice the invention, including making and using any devices or systems and performing any incorporated methods. The patentable scope of the invention is defined by the claims, and may include other examples that occur to those skilled in the art. Such other examples are intended to be within the scope of the claims if they have structural elements that do not differ from the literal language of the claims, or if they include equivalent structural elements with insubstantial differences from the literal languages of the claims. 

1. A polymer blend composition comprising: an impact modified polypropylene copolymer; and a low density polyethylene polymer, a ratio of an amount, by weight, of said impact modified polypropylene copolymer to an amount, by weight, of said low density polyethylene polymer is between about 6:4 to about 9:1.
 2. A polymer blend composition in accordance with claim 1 further comprising up to about 15 percent by weight of a mineral filler, the percent by weight based on the total weight of the composition.
 3. A polymer blend composition in accordance with claim 1 wherein said impact modified polypropylene copolymer comprises a copolymer formed from a propylene monomer and a monomer selected from the group consisting of an ethylene propylene diene monomer, a styrene butadiene monomer, and an isoprene monomer.
 4. A polymer blend composition in accordance with claim 2 wherein said mineral filler comprises at least one of limestone and barites.
 5. A polymer blend composition in accordance with claim 1 wherein said impact modified polypropylene copolymer has a melt flow index at 230° C. of about 0.1 g/10 min to about 10 g/10 min.
 6. A polymer blend composition in accordance with claim 1 wherein said low density polyethylene polymer has a melt flow index at 190° C. of about 0.1 g/10 min to about 10 g/10 min.
 7. A sheet of automotive flooring material comprising a polymeric material, said polymeric material formed from a polymer blend composition comprising: an impact modified polypropylene copolymer; and a low density polyethylene polymer, a ratio of an amount, by weight, of said impact modified polypropylene copolymer to an amount, by weight, of said low density polyethylene polymer is between about 6:4 to about 9:1.
 8. A sheet of automotive flooring material in accordance with claim 7 wherein said polymer blend further comprises up to about 15 percent by weight of a mineral filler, the percent by weight based on the total weight of the composition.
 9. A sheet of automotive flooring material in accordance with claim 7 wherein said impact modified polypropylene copolymer comprises a copolymer formed from a propylene monomer and a monomer selected from the group consisting of an ethylene propylene diene monomer, a styrene butadiene monomer, and an isoprene monomer.
 10. A sheet of automotive flooring material in accordance with claim 8 wherein said mineral filler comprises at least one of limestone and barites.
 11. A sheet of automotive flooring material in accordance with claim 8 wherein said polymer blend composition further comprises up to about 50 percent by weight of reclaimed automotive flooring material, the percent by weight based on the total weight of said polymer blend composition.
 12. A sheet of automotive flooring material in accordance with claim 8 wherein said impact modified polypropylene copolymer has a melt flow index at 230° C. of about 0.1 g/10 min to about 10 g/10 min, and said low density polyethylene polymer has a melt flow index at 190° C. of about 0.1 g/10 min to about 10 g/10 min.
 13. A sheet of automotive flooring material in accordance with claim 8 wherein said sheet of automotive flooring material has a gloss equal to or less than 8 measured at a 60 degree angle.
 14. A method of making an automotive flooring article, said method comprising: providing a polymer blend composition; heating the polymer blend to a temperature of about 340° F. to about 380° F.; extruding the heated polymer blend to form a sheet of automotive flooring material; and cooling the sheet of automotive flooring material; the polymer blend composition comprises: an impact modified polypropylene copolymer; and a low density polyethylene polymer, a ratio of an amount, by weight, of the impact modified polypropylene copolymer to an amount, by weight, of the low density polyethylene polymer is between about 6:4 to about 9:1.
 15. A method in accordance with claim 14 further comprising thermoforming the sheet of automotive flooring material to a desired shape to form the automotive flooring article.
 16. A method in accordance with claim 14 wherein the polymer blend further comprises up to about 15 percent by weight of a mineral filler, the percent by weight based on the total weight of the composition, the mineral filler comprising limestone or barites.
 17. A method in accordance with claim 14 wherein the impact modified polypropylene copolymer comprises a copolymer formed from a propylene monomer and a monomer selected from the group consisting of ethylene propylene diene monomer, a styrene butadiene monomer, and isoprene monomer.
 18. A method in accordance with claim 15 further comprising embossing the sheet of automotive flooring material before thermoforming or during thermoforming.
 19. A method in accordance with claim 14 wherein said extruding the heated polymer blend to form a sheet of automotive flooring material comprises extruding the heated polymer blend to form a sheet of automotive flooring material having a gloss equal to or less than about 8 measured at a 60 degree angle.
 20. A method in accordance with claim 18 wherein said embossing the sheet of automotive flooring material comprises embossing the sheet of automotive flooring material to form a sheet of automotive flooring material having a gloss equal to or less than about 3 measured at a 60 degree angle.
 21. A method in accordance with claim 15 wherein said thermoforming the sheet to a desired shape to form the automotive flooring article comprises thermoforming the sheet to a desired shape to form the automotive flooring article having a gloss equal to or less than about 8 measured at a 60 degree angle when the automotive flooring sheet is not embossed, and having a gloss equal to or less than about 3 measured at a 60 degree angle when the automotive flooring sheet is embossed.
 22. An automotive flooring material comprising a polymeric material, said polymeric material formed from a polymer blend composition comprising: an impact modified polypropylene copolymer comprising a copolymer formed from a propylene monomer and a monomer selected from the group consisting of an ethylene propylene diene monomer, a styrene butadiene monomer, and an isoprene monomer; and a low density polyethylene polymer, a ratio of an amount, by weight, of said impact modified polypropylene copolymer to an amount, by weight, of said low density polyethylene polymer is between about 6:4 to about 9:1, said automotive flooring material having a gloss equal to or less than 8 measured at a 60 degree angle.
 23. An automotive flooring material in accordance with claim 22 wherein said polymer blend further comprises up to about 15 percent by weight of a mineral filler, the percent by weight based on the total weight of the composition.
 24. An automotive flooring material in accordance with claim 23 wherein said mineral filler comprises at least one of limestone and barites.
 25. An automotive flooring material in accordance with claim 22 wherein said polymer blend composition further comprises up to about 50 percent by weight of reclaimed automotive flooring material, the percent by weight based on the total weight of said polymer blend composition.
 26. An automotive flooring material in accordance with claim 22 wherein said impact modified polypropylene copolymer has a melt flow index at 230° C. of about 0.1 g/10 min to about 10 g/10 min, and said low density polyethylene polymer has a melt flow index at 190° C. of about 0.1 g/10 min to about 10 g/10 min.
 27. A sheet of automotive flooring material comprising a polymeric material, said polymeric material formed from a polymer blend composition comprising: a copolymer formed from a propylene monomer and a monomer selected from the group consisting of an ethylene propylene diene monomer, a styrene butadiene monomer, and an isoprene monomer; and a low density polyethylene polymer, said blend comprising about 60 percent by weight to about 90 percent by weight of said copolymer and about 10 percent by weight to about 40 percent by weight of said low density polyethylene polymer.
 28. A sheet of automotive flooring material in accordance with claim 27 wherein said polymer blend further comprises up to about 15 percent by weight of a mineral filler, the percent by weight based on the total weight of the composition.
 29. A sheet of automotive flooring material in accordance with claim 28 wherein said mineral filler comprises at least one of limestone and barites.
 30. A sheet of automotive flooring material in accordance with claim 27 wherein said polymer blend composition further comprises up to about 50 percent by weight of reclaimed automotive flooring material, the percent by weight based on the total weight of said polymer blend composition.
 31. A sheet of automotive flooring material in accordance with claim 27 wherein said copolymer has a melt flow index at 230° C. of about 0.1 g/10 min to about 10 g/10 min, and said low density polyethylene polymer has a melt flow index at 190° C. of about 0.1 g/10 min to about 10 g/10 min.
 32. A sheet of automotive flooring material in accordance with claim 27 wherein said sheet of automotive flooring material has a gloss equal to or less than 8 measured at a 60 degree angle.
 33. A sheet of automotive flooring material in accordance with claim 27 further comprising an embossed surface.
 34. A sheet of automotive flooring material in accordance with claim 33 wherein said sheet of automotive flooring material has a gloss equal to or less than 3 measured at a 60 degree angle. 